Prevest Fusion Self Lute

• Exceptional handling, especially with excess cement removal
• Durability and reliability with all indirect restorations
• High bond strength and excellent marginal sealing
• Low Solubility
• Simple to use, self-adhesive, no primers, silane or bonding agents needed

Composition:

Base Paste: Bisphenol A Glycidyl Methacrylate, Ethoxlated Bisphenol A Dimethacrylate, Triethylene Glycol Dimethacrylate, Silanated Barium Glass Powder, Amorphous Fumed Silica, Curing Agents and Stabilizer.

Catalyst Paste: Bisphenol A Glycidyl Methacrylate, Ethoxlated Bisphenol A Dimethacrylate, Triethylene Glycol Dimethacrylate, Silanated Barium Glass Powder, Amorphous Fumed Silica, Curing Agent and Stabilizer.

Initial set: 2:00-2:30 (min:sec)

Final set: 3-4 minutes

Storage Conditions:

• Store at temperature between 10°C to 24°C.
• Close the cap carefully after use. Keep away from moisture.
• Shelf life not affected after opening if stored in a cool dry place.

Shelf life: 2 years from date of manufacture

• 1 x Automix Syringe 9g
• 10 x Automix Tips

Dispense the material from the syringe through auto mix tip. The initial set will occur in 2:00-2:30 (min:sec) with a final set at 3-4 minutes.

1. Metal to Enamel / Dentin: Metal restorations to tooth structure-crowns, inlays, bridges, and posts including Maryland bridges. After try-in, sandblast each side of the restoration. Using a metal primer of your choice, treat the metal exposed to the paste. Clean tooth with non-fluoridated prophy paste or pumice. To prepare tooth for bonding, use a universal dentin / enamel bonding system. Mix equal amounts of catalyst and base pastes and use a plastic instrument or injection system to place in restoration. Avoid trapping air bubbles. Seat Restoration on tooth and hold in place until paste reaches initial set (about 2:00-2:30 minutes). Use a scaler or explorer to remove excess cement immediately upon initial set. It is important to wait until the final set to remove excess cement.

2. Metal to Metal: Implant prosthesis or crown on post. Sandblast all external metal surfaces to be exposed to paste. Rough intra-oral metal with a micro-etcher or bur. Using a metal primer of your choice, treat the metal exposed to the paste. Clean posts or Abutments with non-fluoridated prophy paste or pumice. Mix equal amounts of catalyst and base pastes and use a plastic instrument or injection system to place in restoration. Avoid trapping air bubbles. Seat restoration on tooth and hold in place until paste reaches initial set (about 2:00-2:30 minutes). Use scaler or explorer to remove excess cement immediately upon initial set. It is important to wait until final set to remove excess cement.

3.Ceramic Restorations to Teeth (Porcelain Veneers, In-lays, On-lays) After try-in, etch ceramic restoration and place in acetone or ethanol in ultrasonic cleaner for 1-2 minutes. Place silanating agent on internal or porcelain restoration. Clear tooth with non-fluoridated prophy paste or pumice. To prepare tooth for bonding, use a universal dentin / enamel bonding system. Mix equal amounts of catalyst and base pastes and use a plastic instrument or injection system to place in Restoration. Avoid trapping air bubbles. Seat restoration on tooth and hold in place until paste reaches initial set (about 2:00-2:30 minutes) use scaler or explorer to remove excess cement immediately upon initial set. It is not important to wait until final set to remove excess cement.

• Country of Origin: India
• Manufacturer: Prevest Denpro

Question: How does the Fusion Self Lute perform regarding bond strength and marginal sealing?
Answer: Fusion Self Lute provides high bond strength and excellent marginal sealing, ensuring durable and reliable restorations.

Question: Do I need to use any additional primers, silane, or bonding agents with Fusion Self-Lute?
Answer: No, Fusion Self Lute is self-adhesive and does not require any additional primers, silane, or bonding agents.

Question: What is Fusion Self Lute?
Answer: Fusion Self Lute is a self-adhesive resin cement designed for exceptional handling and reliable performance with all indirect restorations.