Prevest Denpro Nanoseal-S

• NanoSeal-S is composed of two components which have to be mixed in a 1:1 ratio to obtain a homogenous paste.
• Radiopaque and eugenol free
• Excellent flow and superior bio-compatibility
• Expands by 0.2% to give a tight seal
• It has a working time less than 10 min and setting time of 10-15min.

Technical Data:

1) Mixing Time: 45 - 60 sec.

2) Working Time: <10 min.

3) Setting Time: 10 - 15 min.

4) Flow: 65 mm

5) Solubility: >2%

Composition:

• Polydimethyl siloxane,
• Nano Silver powder,
• Silicone Oil,
• Platinum Catalyst,
• Zirconium Dioxide,
• Paraffin Liquid

Storage Conditions:

• Store at temperature between 10°C to 24°C. Close the cap carefully after use.
• Keep away from moisture. Shelf life not affected after opening if stored in a cool dry
  place.

Shelf life: 3 years from the date of manufacturing.

• 1 x 10g Cartridge (Base/Catalyst)
• 1 x Mixing Spatula
• 1 x Mixing Pad

After shaping and cleaning, root canal should be filled with NanoSeal-S in combination with gutta-percha.

1. After standard root canal preparation, the root canal should be thoroughly irrigated with
sterile water to remove traces of irrigating agents which would interfere with the curing of
NanoSeal-S.

2.The root canal should be thoroughly dried using alcohol/ paper points .

3. The sealer must be dispensed from the dual barrel syringe in a 1:1 ratio. The sealer must be
mixed thoroughly to be make a void free homogenous mix.

4.The root canal can be coated with NanoSeal-S using a gutta-percha point or a paste carrier.

5. NanoSeal-S has a working time less than10 min and a setting time of 10-15 min.

6. Use of heated instruments can accelerate the setting of NanoSeal-S.

7. After use, the dual barrel syringe must be thoroughly cleaned using a tissue paper and
properly sealed to avoid contamination. 

• Country of Origin: India
• Manufacturer: Prevest Denpro

Question: What is the recommended mixing time for NanoSeal-S?
Answer: The recommended mixing time is 45 - 60 seconds.

Question: Can NanoSeal-S be removed during retreatment?
Answer: Yes, NanoSeal-S can be removed by conventional methods. The sealer does not chemically adhere to dentine. Heat, gates glidden drills, and paeso-reamers are recommended for the removal of gutta-percha during post-space preparation and retreatment.

Question: How does NanoSeal-S enhance antibacterial efficiency?
Answer: Nano silver is incorporated into the sealer, which enhances its antibacterial efficiency and acts as a preservative.

Question: What are the key features of NanoSeal-S?
Answer: NanoSeal-S is a self-curing, antibacterial root canal sealer fortified with nano silver. It provides excellent sealing ability, superior radio-opacity, and superior biocompatibility.

Question: What is NanoSeal-S?
Answer: NanoSeal-S is a cold flowable polydimethylsiloxane-based root canal sealer with micro silver in chemical form.